HOME > 제품소개 > 쎈코트
2-Coat system (2C 1B)
Substrate | Pretreatment | Method of Application |
Coating System |
Product Name |
D.F.T (㎛) |
Baking condition (KEEP TIME |
---|---|---|---|---|---|---|
Aluminum | Chromate | Spray | Primer | DSS-130 | 7~10 | SET 10min |
Top | NEW SSENCOAT | 25~30 | 180℃ X 15min |
3-Coat system (3C 2B)
Substrate | Pretreatment | Method of Application |
Coating System |
Product Name |
D.F.T (㎛) |
Baking condition (KEEP TIME |
---|---|---|---|---|---|---|
Aluminum | Chromate | Spray | Primer | DSS-130 | 5~10 | SET 10min |
Top | NEW SSENCOAT | 25~30 | 180℃ X 15min | |||
Clear | NEW SSEN Clear | 10~15 | 180℃ X 15min |
Description | Requirement | Result | |
---|---|---|---|
광택(60º Gloss) | 유,반,무광 | 지정광택 | |
도막경도(Dry film hardness) | 3H이상 | 3H | |
부착성 (adhesion) | Dry, wet boiling water, No removal | No removal | |
내충격성 (Impact resistance) | 5/8" distortion, No removal | No removal | |
내마모성 (abrasion resistance) | abrasion coeffcient value, 40min | Exceeds spec | |
내상성 (acid resistance) | 10% Muriatic acid, 15min no visual changes |
No Blistering, No Visual change | |
내몰탈성 (Mortar resistance) | Mortar pat, 24hr, no visual change | No Visual change | |
내질산성(Nitric acid resistance) | 70% - HNO₃ Vapor 30min △E<5 color mac change |
5△E | |
내세제성 (Detergent resistance) | 3% Detergent 72hrs no effect | No Blistering, No Visual change | |
내습성 (Humidity resistance) | RH 100%, 38℃, 3000hrs Blister not to exceed No.8 |
No Blistering | |
내염수분무성 (Salt spray resistance) | 5% salt 3000hr, minimum 7 rating on scribe or cut rating of 8 and minimum blister rating of 8 |
No Blistering | |
총진내후성 (Accelerated weathering resistance) |
W.O.M (3,000시간) 광택보존성 (Gloss retention) |
△E<5 85% 이상 |
△E<5 85% |
Q.U.V (3,000시간) 광택보존성 (Gloss retention) |
△E<5 85% 이상 |
△E<5 85% |