HOME > 제품소개 > 불소도장
도장 시스템 | 공정 | 품명 | 건조도막두께 | 건조 조건 |
---|---|---|---|---|
2-COAT SYSTEM |
Primer | FROPON(S) Primer | 5-10 | 210-2161c x 5mins |
FROPON(S) Flash Primer | Flash-off | |||
Top | FROPON(S) Color | 25-30 | 232-2411C xIOmins | |
2-COAT PEARL SYSTEM |
Primer | FROPON(S) Primer | 5-10 | 210-2161C x 5mins |
FROPON(S) Flash Primer | Flash-off | |||
Top | FROPON(S) P Color | 30-35 | 232-241 社 xIOmins | |
3-COAT SYSTEM |
Primer | FROPON(S) Primer | 5-10 | 210-216°c x 5mins |
FROPON(S) Flash Primer | Flash-off | |||
Top | FROPON(S)XM Color | 25-30 | 232-241^ xIOmins | |
Flash-off | ||||
Clear | FROPON(S) Top Clear | 10-15 | 232-24113 xIOmins |
Properties | Description | Remarks | Result | |
---|---|---|---|---|
광택 | 60° Glass | ASTM D523 | Spec, ±5 | |
연필경도 | Berol Eagle Turquoise Pencil | ASTM D3363 | F Min. | |
부착성 | Dry Adhesion | 1mm Cross Cut | ASTM D3359 | 100/100 |
Wet Adhesion | 38°c, 24hrs, 1mm Cross Cut | |||
Boiling Water Adhesion | 100°c, 20mins, 1mm Cross Cut | |||
충격성 | 5/8inch Diameter 0.1inch Distortion |
ASTM D2794 | No Removal | |
내마모성 | Falling Sand | ASTM D968 | 40min. | |
내몰탈성 | Mortar PAT 24hrs | AAMA 2605 | Novisual Change No Blistering | |
내세제성 | 3% Detergent, 38°c, 72hrs | ASTM D2248 | No Blistering (ASTM D3359) | |
내유리세정성 | 10Drops, 24hrs Cross-Cut |
AAMA 2605 | Novisual Change No Blistering |
|
내산성 | Muriatic Acid Resistance | 10% muriaticacid, 15mins | AAMA 2605 | Novisual Change No Blistering |
Nitric Acid Resistance | 70% HNO3, 30mins | ASTM D2244 | △E = 5 Max | |
내습성 | HR 100%, 38°c, 4000hrs | ASTM D2247 | Blister Size No.8 Max (ASTM D714 |
|
내염수분무성 | 5% Salt Solution, 4000hrs | ASTM B117 | Scribe or Cut edges : rating 8Min Field : rating 7Min (ASTM D1654) |
|
내후성 | Color Retention | South Florida 10years Exposure |
ASTM D2244 | △E = 5 Max |
Glass Retention | ASTM D523 | 50% Min. | ||
Chalk Resistance | ASTM D659 | Rating 6-8 | ||
Resistance To Erosion | ASTM B244 | Film loss 10% |